The 1050 aluminum alloy is formed from pure aluminum by added a small amount of copper element, and the 1050 aluminum sheet has low strength, excellent formability, surface treatment property, weldability and corrosion resistance. Besides, the industrial pure aluminum has the characteristics of high plasticity, corrosion resistance, electrical conductivity and thermal conductivity, but the strength is low, it can ...
1050 aluminium alloy is an aluminium-based alloy in the "commercially pure" wrought family (1000 or 1xxx series). As a wrought alloy, it is not used in castings. Instead, it is usually formed by extrusion or rolling. It is commonly used in the electrical and chemical industries, on account of having high electrical conductivity, corrosion resistance, and workability. 1050 alloy is also sometimes used for the manu ...
5083 Aluminum Alloy – Supplied in sheet marine grade tempers H116, H321, H323; to spec ASTM B928. Tempers.O, H112, H32; to spec ASTM B209, and extrusion shapes in various tempers and specifications. This is an excellent marine environment corrosion resistant aluminum alloy, It is primarily an alloy used for its corrosion resistant properties as it is especially good on inter granular corrosion resistance. Also, t ...
Alloy temper
Coefficient of thermal expansion (20)μm/m.k
Melting point range(℃)
Conductivity
( %IACS )
Resistivity
Ωmm2/m
Density (g/cm3) 5052 H112
23.2
500 - 635
30
0.058
2.82 5083 H112
23.8
607 - 650
35
0.050
2.72 6061 T651
23.4
570 - 640
29
0.059
2.72 7050 T7451
23.6
580 - 650
43
0.040
2.73 7075 T651
23.5
490 - 630
41
0.0415
2.82 2024 T351
23 ...
1050 aluminium alloy is an aluminium-based alloy in the "commercially pure" wrought family (1000 or 1xxx series). As a wrought alloy, it is not used in castings. Instead, it is usually formed by extrusion or rolling. It is commonly used in the electrical and chemical industries, on account of having high electrical conductivity, corrosion resistance, and workability. 1050 alloy is also sometimes used for the manu ...
3105-H14 aluminum is 3105 aluminum in the H14 temper. To achieve this temper, the metal is strain hardened to a strength that is roughly halfway between annealed (O) and full-hard (H18). The graph bars on the material properties cards below compare 3105-H14 aluminum to: 3000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relev ...