Aluminum Alloy 6061 sheets are the most versatile of the heat treatable aluminum alloys. Though less strong than most of the 2000 and 7000 alloys, 6061 aluminum provides an extensive range of mechanical properties and corrosion resistance and can be fabricated by many of the commonly used practices. In the “”O”” temper or annealed condition, alloy 6061 has good formability. In the T4 condition, fairly severe forming can be done; whereas, in the T6 condition, properties may be obtained by artificial aging.
6063 aluminum sheet is very similar to 6061 aluminum sheet. The main alloying elements of 6063 aluminum alloy are magnesium and silicon, which have excellent processing performance, excellent weld-ability, good mechanical properties, extrusion and plating, good corrosion resistance, toughness, easy polishing, upper coating, and excellent anodizing effect. The most common used temper of aluminum sheet 6063 is T1, T5 and T6, 6063 has an ultimate tensile strength with every temper. The thickness of aluminium sheet 6063 is 0.3 to 600 mm, the width is 500 to 2600 mm, the length is 500 to 16000 mm.
6061 aluminum sheet alloy is strong, easily machined, and weldable. Aluminum 6061 T6 alloys are doubled the strength of aluminum 6063 alloys. Aluminum 6061 has an ultimate tensile strength of at least 42,000 psi (290 MPa) and yield strength of at least 35,000 psi (241 MPa). In thicknesses of 0.250 inch (6.35 mm) or less, it has elongation of 8% or more; in thicker sections, it has elongation of 10%. T651 temper has similar mechanical properties. The famous Pioneer plaque was made of this particular alloy. Order 6061 Aluminum Sheets in 6061 Aluminum in small quantities and no minimums of all Aluminum 6061 at The Metal Store. “”