5밀리미터의 알루미늄 판은 구부리기만 하면 너무 많이 구부릴 수 있으며, 알루미늄 판의 품질은 관련이 없습니다..

가장 먼저, 가장 중요한 상태입니다, 상태는 강성과 반경질로 나뉜다, 부드러운 상태 (O 주라고 불리는 일반적으로 평화로운 주) 모든 복잡한 굽힘 효과 기본 행은 아닙니다. (알루미늄 판의 상태는 H18입니다., H19, H38 모두 어렵네요) half-hard state of the aluminum plate can be basically bending (H24 is semi-rigid) O state of bending is certainly no problem, but because is too soft, Basically, with this state to bend less, followed by you want to choose pure aluminum or alloy aluminum pure aluminum hardness is not very good, ~와 함께 1100, 1050, 1060 등등, it is recommended to use 1100H26 alloy aluminum hardness is better, can use 3003, 3005, 5052 and another semi-hard state can be.

Specific circumstances suggest sample to determine, if, ~와 함께 6061, 2024, 7075, due to the hardness is too high, especially the T6 state, more should bend, not unless you turn up the heat to fold, poor good aluminum sheet and aluminum sheet is the difference between the oxidation performance, tolerance, surface effect and the accuracy of the crystal and the uniform stability of distinguishing, bending effect is little different from that alone.

If the quality of baking paint on the aluminum surface is not too good, it is also a waste of good use. It is suggested to use 3003-H26, 3005H24, or 5052H34.