Verfahren zur Oberflächenkratzbehandlung von Aluminiumplatten

Kratzer auf der Oberfläche von Aluminiumplatten treten eher bei der Verarbeitung von Aluminiumplatten auf. Sie wird oft durch unsachgemäße Verarbeitung und Behandlung verursacht, wodurch die Oberfläche beschädigt wird, was die Ästhetik der Aluminiumplatte ernsthaft beeinträchtigt. jedoch, die kratzer sind schon erschienen. Das Folgende beschreibt die Oberflächenkratzbehandlung der Aluminiumplatte. Methode.

The surface scratches of aluminum plates can be treated. In short, there are two methods: physical and chemical: the physical method is mechanical polishing, and the details include sandblasting and wire drawing. This method is generally used for deeper scratches. Chemical methods generally use chemical reagents for polishing. In short, chemical reagents are used to corrode the surface of aluminum. The scratches have sharp edges and the corrosion speed is fast. Lighter scratches can be completely eliminated after chemical polishing. , The chemically polished material has a bright and beautiful appearance. Allgemein, the two methods are used together, and the appearance of the aluminum material can achieve a good decorative effect.

The solution to the scratch on the surface of the aluminum plate:

  • The working belt on the alloy aluminum plate mold needs to be polished and smooth, whether the empty knife of the extrusion mold is enough, and the surface is smooth.
  • In the process of producing alloy aluminum plates, pay attention to the production of mold lines. Once the lines are generated, the mold needs to be loaded in time to stop production.
  • In the process of aluminum plate sawing: each sawing needs to clean the cutting sawdust in time. Prevent secondary scratches.
  • Ähnlich, in the process of CNC machining aluminum plates, it is also necessary to prevent the aluminum slag remaining on the fixture from being scratched.
  • There are exposed industrial aluminum profiles or graphite strips on the discharge track or swing bed with hard inclusions. Avoid scratches on the surface of the aluminum plate when hard debris comes in contact with the aluminum plate.
  • In the process of production and handling, handle with care, try to avoid dragging or flipping the alloy aluminum plate at will.
  • Arrange the aluminum plates reasonably to avoid friction with each other as much as possible.