무엇인가요 7075 알루미늄 시트?
7075 alloy metal aluminum sheet plate is a common alloy in 7000 series aluminum alloy sheet. 7075 알루미늄 시트 (Al-Zn-Mg-Cu) belongs to super-hard aluminum. As a kind of cold finished wrought alloy, it has great strength and hardness. It’s far better than mild steel. This alloy has good mechanical properties and anode reaction. 7075 aluminum sheet as a typical kind of aerospace aluminum alloy material is usually used for high-end fields.
Zinc is the main alloy element in 7075 알루미늄 판. Adding magnesium to the alloy containing 3% – 7.5% zinc can form mgzn2 with significant strengthening effect, which makes the heat treatment effect of the alloy far better than that of aluminum zinc binary alloy.
Increasing the content of zinc and magnesium in 7075 aluminum plate will further improve the tensile strength, but its ability to resist stress corrosion and spalling corrosion will decrease. After heat treatment, it can achieve very high strength characteristics.
7075 aluminum plate is generally made of a small amount of copper, chromium and other alloys. 그 중, 7075-T651 aluminum alloy is particularly top-grade. It is known as an excellent product of aluminum alloy, with high strength and far better than any mild steel.
7075 aluminum plate characteristics 7075 aluminum plate characteristics
(1) High strength heat treatable alloy;
⑵ Good mechanical properties;
(3) good usability;
(4) Easy to process, good wear resistance;
⑸ Good corrosion resistance and oxidation resistance.
7075 aluminum plate is a kind of high-strength alloy, its emergence has helped a lot of the manufacturing industry, and has made the greatest contribution to the development of human aviation.
7075 Aluminum Sheet properties by temper
| 합금 |
성질 |
두께(mm) |
너비(mm) |
길이(mm) |
Typical products |
| 7075 알루미늄 시트 |
영형、T6、T651 |
0.2-300 |
<1500 |
<8000 |
Golf head, 곰팡이, aircraft landing gear and other |
7075 Aluminum Sheet Chemical Composition Limits
화학 성분 제한 (%)
| 규소 |
0.4 |
| 철 |
0.5 |
| 구리 |
1.2-2.0 |
| 망간 |
0.3 |
| 마그네슘 |
2.1-2.9 |
| 크롬 |
0.18-0.28 |
| 아연 |
5.1-6.1 |
| 티탄 |
0.2 |
| 기타, each |
0.05 |
| 기타, total |
0.15 |
| 균형, 알류미늄 |
– |
7075 Aluminum Sheet Mechanical properties
Properties of 7075 알루미늄 합금: cold treated forging alloy has high strength, which is much better than mild steel.
7075-0 알루미늄 시트
Un-heat-treated 7075 （7075-0 temper） has maximum tensile strength no more than 280 MPa （40，000 psi）， and maximum yield strength no more than 140 MPa （21，000 psi）。 The material has an elongation （stretch before ultimate failure） of 9–10%. It is very highly corrosion-resistant and has good strength.
7075-T6 Aluminum Sheet
T6 temper 7075 has an ultimate tensile strength of 510–540 MPa （74，000–78，000 psi） and yield strength of at least 430–480 MPa （63，000–69，000 psi）。 It has a failure elongation of 5–11%.
The T6 temper is usually achieved by homogenizing the cast 7075 at 450 °C for several hours， quenching， and then aging at 120 °C for 24 시간. This yields the peak strength of the 7075 합금. The strength is derived mainly from finely dispersed eta and eta‘ precipitates both within grains and along grain boundaries.
7075-T651 Aluminum Sheet
T651 temper 7075 has an ultimate tensile strength of 570 MPa （83，000 psi） and yield strength of 500 MPa （73，000 psi）。 It has a failure elongation of 3–9%. These properties can change depending on the form of material used. Thicker plate may exhibit lower strengths and elongation than the numbers listed above.
7075 알루미늄 시트
7075-T7 Aluminum Sheet
T7 temper has an ultimate tensile strength of 505 MPa （73，200 psi） and yield strength of 435 MPa （63，100 psi）。 It has a failure elongation of 13%.T7 temper is achieved by overaging （meaning aging past the peak hardness） the material. This is often accomplished by aging at 100–120 °C for several hours and then at 160–180 °C for 24 hours or more. The T7 temper produces a micro-structure of mostly eta precipitates. In contrast to the T6 temper， these eta particles are much larger and prefer growth along the grain boundaries. This reduces the susceptibility to stress corrosion cracking. T7 temper is equivalent to T73 temper.
7075-RRA Aluminum Sheet
The retrogression and reage （RRA） temper is a multistage heat treatment temper. Starting with a sheet in the T6 temper， it involves overaging past peak hardness （T6 temper） to near the T7 temper. A subsequent reaging at 120 °C for 24 hours returns the hardness and strength to or very nearly to T6 temper levels.
RRA treatments can be accomplished with many different procedures. The general guidelines are retrogressing between 180–240 °C for 15 분 10 에스.
7075 알루미늄 판, T7351, and T651 state difference
Is two states, T651 is the artificial aging state after solution treatment first, and then tensile treatment to eliminate the residual stress after solution treatment; T7351 is graded aging after solution treatment. Tensile treatment is carried out to eliminate residual stress after solution treatment. The strength of T7351 is lower than that of T651, and the corrosion resistance is significantly improved.
신청 7075 알루미늄 시트
7075 super-hard alloy is the most representative one of the 7000 시리즈, and is usually used as welding or aircraft materials. 7075 aluminum sheet is used for manufacturing of high-strength aircraft structures and other high-stress structural parts with great strength and strong corrosion resistance, such as lower wing panel, stringers, and frame of the aircraft.
내 근처의 알루미늄 시트 제조업체
허난 화웨이 알루미늄 주식회사, 주식회사. 중국의 많은 알루미늄 제조업체 및 공급업체의 리더입니다.. 우리는 품질을 엄격하게 관리하고 고객에게 중점을 둡니다.. 우리는 귀하와 심층적인 협력을 갖고 고품질의 알루미늄 소재 제품 맞춤형 OEM 서비스를 제공하기를 희망합니다.. kg당 최신 최저가를 알고 싶다면 ( 킬로그램 ) 또는 표준 중량 톤당, 문의하시기 바랍니다.
알루미늄 시트 플레이트 표준 수출 포장
- 알루미늄 판은 클립 또는 라미네이트 처리되어 알루미늄 판의 표면이 손상되지 않고 흠집이 없는지 확인합니다.;
- 플라스틱 필름 ( HDPE, PVC, PE 또는 PET 등 ) 습기와 비를 방지하기 위해 보호 또는 하드 크라프트지 포장을 사용하여 운송 중에 알루미늄 판이 깨끗하고 먼지가 없는지 확인합니다. (각 패키지에는 중국 동부 및 남부 지역에서 제품의 품질을 보장하기 위한 방습 건조제가 포함되어 있습니다., 비가 더 많이 오는 곳);
- 운송 중 충돌을 방지하고 알루미늄 판의 기하학적 구조가 변경되지 않도록 보장하기 위해 나무 브래킷으로 설치하고 강철 스트랩으로 강화했습니다.;
- 수출제품의 경우, 우리는 포장을 위해 훈증 표시가 있는 나무 상자와 팔레트를 사용합니다.;
- 우리는 또한 고객의 다른 포장 요구 사항에 따라 포장할 수 있습니다.;