3105 h24 aluminum properties

2019-02-13

3105-H24 aluminum is 3105 aluminum in the H24 temper. To achieve this temper, the metal is strain hardened to a strength that is roughly halfway between annealed (O) and full-hard (H18). The graph bars on the material properties cards below compare 3105-H14 aluminum to: 3000-series alloys (top), all aluminum alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Aluminum 3105 alloy has good forming characteristics. It is suggested that bend radii should be used in one thickness to 2 t range for annealed H12, H14 and H16 tempers. Bend radii of 2 to 7 t should be used for the H18 temper.

Aluminum 3105 alloy can be forged at the temperatures ranging from 372 to 510°C (700 to 950°F). Aluminum 3105 alloy can be hot worked at 205 to 372°C (400 to 700°F) Aluminum 3105 alloy has good cold working characteristics in the harder cold worked tempers. Aluminum 3105 alloy is annealed at 344°C (650°F) followed by cooling in air. Aluminum 3105 alloy can be hardened only by cold working in H12, 14, 16, 18 or 25 tempers.


TAG: en aw 3003 3003 h22 aluminum properties 3003 vs 3004 aluminum 3003 aluminum vs 6061 3003 aluminum vs 5052 3004 aluminum 3004 aluminum properties 3004 aluminum cookware 3004 aluminum alloy 3005 aluminum en aw 3103 3105 aluminum 3105 h14 aluminum 3105 h24 aluminum 3105 aluminum alloy 3105 aluminum sheet