1100 metal pure aluminum sheet plate

1100 aluminum sheet plate overview

1100 aluminum sheet plate belongs to 1xxx series aluminum sheet, which  is one of the softest aluminum alloys, so it is not used for high strength or high pressure applications. Although pure aluminum is usually cold-worked, it can also be hot-worked, but it is more common that aluminum is formed through spinning, stamping, and drawing processes that do not require the use of high heat. These processes produce aluminum profiles in the form of foils, plates, round bars, sheets, strips and wires.

Aluminum 1100 can also be welded; resistance welding is possible, but it can be difficult and usually requires the attention of a skilled welder. Aluminum 1100 is just one of several common aluminum alloys. It is soft, low-strength, and the smallest aluminum at 99% is commercial pure aluminum. Copper, iron, magnesium, manganese, silicon, titanium, vanadium and zinc constitute the remaining elements. It cannot be hardened by heat treatment and is very formable.

1100 metal pure aluminum sheet plate

1100 aluminum alloy is ordinary industrial pure aluminum with 99.0% aluminum content. It cannot be strengthened by heat treatment; the strength is low, but it has good ductility. Formability, weldability and corrosion resistance; after anodic oxidation, the corrosion resistance can be further improved while obtaining a beautiful surface.

1100 aluminum sheet is the most commercially pure alloy of all the aluminium grades. 1100 aluminium coil and 1100 aluminium sheet are both available for various applications including chemical storage and processing equipemtn. Benefits of 1100 aluminium coil & sheet include a 99% or greater content of aluminium compared to other grades of aluminium. 1100 is a low strength aluminium alloy with excellent corrosion resistance. This grade is best used for welding, brazing and soldering but has poor machinability. 1100 aluminium has great finishing capabilities so it is a great choice for decorative purposes.

1100 aluminum sheet parameters

Equivalent name

a1100, 1100a, aa1100, 1100aa, al1100, al1100a, 1100 aa, aa 1100, jis a1100p, al1100 class, aw1100 grade etc

Temper

Soft HO, H11, H12, H13, H14, H15, H16, H17, H18, H19, H20, H21, H22, H23, H24, H25, H26, H27, H28, H29, H30, H31, H32, H33, H34, H35, H36, H37, H38, H39, H46, H111, H112, H114, H116, H131, H321 etc

Thickness: ( thin) 0.18mm, 0.5mm, 0.8mm, 1mm, 1.5mm, 1.8mm, 2mm, 3mm, 3.8 mm, 4mm, 8mm ( thick ) etc

Size: 4ft x 8ft etc

Surface treatment: anodized, colored coated, embossed etc

Chemical composition of 1100 aluminum sheet

Si ( Silicon )	Cu ( Copper )	Mg ( Magnesium )	Zn ( Zinc )	Mn ( Manganese )	Cr ( Chromium )	Fe ( Iron )	Ti ( Titanium )	Other	Others total	Al ( Aluminum )
≤ 0.95	≤ 0.05	≤ 0.05	≤ 0.1	≤ 0.05	/	≤ 0.4	/	≤ 0.05	≤ 0.15	remainder

Properties of 1100 aluminum flat plates

Alloy Temper

Specified

Tensile strength

Yield strength

Elongation

Thickness(in.)

(ksi)

(ksi)

(%)

1100-O (annealed)

0.006-0.019

11.0-15.5

Min3.5

Min15

0.020-0.031

Min20

0.032-0.050

Min25

0.051-0.249

Min30

0.250-3.000

Min28

1100-H12/1100-H22

0.017-0.019

14.0-19.0

Min11.0

Min3

0.020-0.031

Min4

0.032-0.050

Min6

0.051-0.113

Min8

0.114-0.499

Min9

0.500-2.000

Min12

1100-H14/1100-H24

0.009-0.012

16.0-21.0

Min14.0

Min1

0.013-0.019

Min2

0.020-0.031

Min3

0.032-0.050

Min4

0.051-0.113

Min5

0.114-0.499

Min6

0.500-1.000

Min10

1100-H16/1100-H26

0.006-0.019

19.0-24.0

Min17.0

Min1

0.020-0.031

Min2

0.032-0.050

Min3

0.051-0.162

Min4

1100-H18/1100-H28

0.006-0.019

Min22.0

–

Min1

0.020-0.031

Min2

0.032-0.050

Min3

0.051-0.128

Min4

1100-H112

0.025-0.499

Min13.0

Min7.0

Min9

0.500-2.000

Min12.0

Min5.0

Min14

2.001-3.000

Min11.5

Min4.0

Min20

Applications of 1100 aluminium plain sheets

1100 aluminum sheet is mostly used for some parts which require good forming and processing properties, high anti-corrosion, but low strength, such as video, the transportation and storage equipments of chemical products, metal sheet products, the processing of drawing spinning hollow goods, welding key combination, reflector and nameplat, etc. 1100 aluminum sheet is widely used in various fields from cooking utensils to industrial equipment, such as heat sinks, caps, printing sheets, building materials, heat exchanger components, it can also be used as deep-draw stamping products.

Cold rolled is the most commonly used forming method for aluminum 1100. A cold metal working process is any metal forming or forming process performed at or near room temperature. Aluminum 1100 can be processed into many different products, including chemical equipment, railroad tank cars, shark fins, dials, nameplates, cookware, rivets, reflectors, and metal plates. The plumbing and lighting industries also use aluminum 1100, as do many other industries.

Kitchen utensils ( cooker ), building materials, heat exchangers etc.

• 1100 plain alu sheet raw material for perforated sheet
• 1100 al sheet plate for aluminium gusset plate
• 4ft 1100 aluminum sheet for kitchen utensils
• Color coating 1100 aluminum sheet for building materials
• Heat exchangers
• 1100 aluminum sheet for bus body
• 1100 thermal insulation aluminum plate