Die Produktionstechnologie von 6082 Aluminiumblech

Die Produktionstechnologie von 6082 Aluminiumblech.Wir bieten 6082 Aluminiumlegierung in bar, Teller, Rohre und Extrusionen.

6082 gehört zu den 6000 Serie (Al-Mg-Si) Aluminiumlegierungsblech. Es ist eine Art Aluminiumlegierungsblech, das durch Wärmebehandlung verstärkt werden kann. Es hat eine mittlere Stärke, gute Schweißbarkeit und Korrosionsbeständigkeit. Es wird hauptsächlich in der Transport- und Hochbauindustrie verwendet. Such as bridges, Kräne, roof frames, Transportflugzeuge, Transportschiffe, etc.6082 aluminium alloy offers good machinability with excellent corrosion resistance. Available in bar, Teller, sheet and tube, the alloy is used in structural applications and is preferred to 6061 aluminum.6082 aluminum sheet plate is used predominantly in highly stressed applications such as trusses, cranes and bridges.

The alloy offers excellent corrosion resistance and has replaced 6061 in vielen Anwendungen. The extruded finish is not as smooth and therefore not as aesthetically pleasing as other alloys in the 6000 series.The production technology of 6082 Aluminiumblech:The first is smelting, 6082 aluminium alloy is characterized by Mn, Mn ist ein hochschmelzendes Metall, smelting temperature should be controlled at 740-760 Grad Celsius. The sample should be evenly stirred for more than two times before sampling to ensure that the metal is completely melted, the temperature is accurate and the composition is uniform.

Nach dem Rühren, one sample is taken at the middle of the molten aluminum depth, the left and right sides of the furnace to analyze, and the converter is folded and qualified; zweitens, im Reinigungs- und Gießprozess, the melt is transferred to the static furnace, then powder injection and jet refining are carried out with nitrogen and refining agent, the refining temperature is 735-745 C, and the refining time is 15 Protokoll. Nach dem Verfeinern, the converter is left standing for 30 Protokoll. Durch diesen Prozess, Gas entfernen, remove slag and purify melt. There are two filters between the casting mold and the furnace mouth. The furnace mouth has a foam ceramic filter plate (30PPI) to filter. Vor dem Gießen, 14 mesh fiberglass cloth is used to filter out the oxide and slag in the melt.