Wieso den 2024 T3-Aluminiumblech kann Flugzeuge verwenden?

Aluminium oder Aluminiumlegierungen sind starke korrosionsbeständige Materialien. Diese Legierungen sind empfindlich gegenüber hohen Temperaturen, die von 200 zu 250 Grad Celsius, verdienen sich die beschreibung, gute Tieftemperaturlegierungen. Ihre Festigkeit nimmt zu, wenn sie Minustemperaturen ausgesetzt wird, und die Festigkeit wird verringert und geht bei hohen Temperaturen verloren.

ALUMINIUM 2024

Aluminiumlegierung 2024 is an aluminum alloy, the primary alloying element being copper. Its main use is in applications that require high strength to weight ratio and good resistance to fatigue. It has the property to be welded but only through friction welding.

Aluminiumlegierung 2024 is annealed from a heat-treated condition between 399 und 427 degrees Celsius for approximately 2 Std, after which it is slowly cooled in the furnace. Alternative, Aluminiumlegierung 2024 can be annealed between cold working operations at 343 degrees Celsius for 2 hours and cooled in air.

2024 t3 aluminum sheet APPLICATIONS

Aluminiumlegierung 2024 is one of the best known high-strength aluminum alloys attributed to its high strength and excellent resistance to fatigue. With such properties and characteristics, it is extensively and commonly used in the following applications:

Aircraft structural components (wing and fuselage structures under tension)

Flugzeugbeschläge

Hardware

Truck wheels

Parts for the transportation industry

Aluminiumlegierung 2024 in plate forms are used in shear webs and ribs, fuselage structures, wing tension members and other structural areas which require stiffness, fatigue performance and good strength. On the other hand, Aluminiumlegierung 2024 in sheet forms, are used in commercial and military aircraft for fuselage skins.

2024 t3 aluminum sheet PROPERTIES

In general, any kind of welding is not recommended for aluminum alloy 2024 because of the resulting degradation of corrosion resistance that occurs as a result of weld heat. In the event that the alloy is welded without using inert gas, the heat treatment should be repeated. Aluminiumlegierung 2024 can be forged but a subsequent heat treatment is needed to retain a reasonable corrosion resistance.

MACHINABILITY AND FORMING

This alloy has good machining properties in the heat-treated condition and in the annealed condition. Hot forming is not allowed for this aluminum alloy 2024. Aluminium 2024 alloy is age-hardening and the heat treatment process will strengthen the alloy even more.

Do you now know enough about aluminum alloy 2024?