How to produce of 6063 aluminium sheet

2019-03-18

Forging 6063 aluminium sheet coil can be done using a temperature set between 750 and 900 degrees Fahrenheit. Temperatures to use for hot working should be between 500 and 700 degrees Fahrenheit. Any common welding technique can be used for this metal.

If annealing is needed, it should be performed continuously at 775 degrees Fahrenheit for between two and three hours, then provide controlled cooling at 50 degrees Fahrenheit per hour, then down to 500 degrees Fahrenheit before air cooling. Aging precipitation heat treatment can also be performed on this grade of aluminum, which should be performed at a 350 degrees Fahrenheit for eight hours before air cooling. This will give it a T6 temper. Heat treatment is another method that can be used to form this alloy. It is recommended that 990 degrees Fahrenheit be used for a long enough time to allow the metal to thoroughly heat, then water quench.

6063 aluminium sheet coil is a general purpose alloy that’s made with silicon and magnesium. It has great resistance to corrosion, higher than other heat treated aluminums, but has lower strength. It has great machinability and forming properties. It can be easily welded and offers great joining characteristics. This aluminum alloy can be anodized and can have other coatings applied. The electrical conductivity of this metal is 40 percent of copper.


TAG:6063 aluminum aluminium 6063 mechanical properties aluminum 6063 t5 vs t6 6063 t4 aluminium alloy 6063 t6 specification 6063 aluminium alloy aluminium 6063 price 6063 aluminum sheet 6063 aluminum properties 6063-t5 aluminum properties 6063 t6 aluminum properties 6063-t6 aluminum alloy 6063 t5 aluminum alloy en aw 6063 en aw 6063 t5 en aw 6063 t6 6063 aluminum vs 6061 6063 vs 6061 6063 t5 vs 6061 t6


Related products